Posted: Fri Dec 17, 2004 1:03 pm Post subject: Welding of Steel Structures |
|
|
Dear Sefians
Generally a base plate and a Cap plate is provided at bottom and at top of steel columns consisting of I sections. These plates are welded with girder. Heat produced at the time of welding makes both ends of column brittle. Incase of earthquake this could be the cause of sudden failure. Is there any alternative to this problem.
Daljeet Sidhu
---------------------------------
Posted via Email |
|
Back to top |
|
 |
nycindia2000 SEFI Member

Joined: 26 Jan 2003 Posts: 12
|
Posted: Sat Dec 18, 2004 10:28 am Post subject: Welding of Steel Structures |
|
|
Dear Fellow Engineer Mr. Daljeet Sidhu, I think this problem of brittleness developed at the joint of base plate/cap plate and I section due to the heat produced during welding can be solved by Normalising process. I hope this solves your Problem. With Best Wishes N.Y.Choudhary
sidhudaljeet@yahoo.com wrote:
Dear Sefians
Generally a base plate and a Cap plate is provided at bottom and at top of steel columns consisting of I sections. These plates are welded with girder. Heat produced at the time of welding makes both ends of column brittle. Incase of earthquake this could be the cause of sudden failure. Is there any alternative to this problem.
Daljeet Sidhu
---------------------------------
Yahoo! Mail - Helps protect you from nasty viruses.
What use is to speak of freedom if people are not ready to sacrifice for it.
Posted via Email |
|